The effect of electron irradiation on the electrical properties of the alloy EVA / LDPE containing soot particles and zinc oxide were studied. The alloy of EVA, with 18 % vinyl acetate (EVA) was used. Due to the EVA polymer microstructure was used for crosslinking and gel caused by electron irradiation test was obtained gel. Dielectric strength and electrical resistance properties of the alloy surface was measured before and after irradiation. In the samples containing zinc oxide after exposure gel and as a result, dielectric strength and a higher level of electrical resistance was observed.
چکیده به فارسی
اثر پرتو الكترون بر خواص الکتريکی آلياژ EVA/LDPE حاوی ذرات دوده و اکسيد روی مورد بررسي قرار گرفت. در اين آلياژ از EVA داراي 18 درصد وزني وينيل استات (EVA) استفاده شد. پليمر EVA به دليل ريزساختار مناسب براي ايجاد اتصالات عرضي مورد استفاده قرار گرفت و ميزان ژل ايجاد شده در اثر پرتودهي الكترون از طريق آزمون ژل به دست آمد. خواص استحکام دی‌الکتريک و مقاومت الکتريکی سطحی آلياژ قبل و بعد از پرتودهي اندازه‌گيري و مقايسه شد. مشاهده گرديد نمونه‌های حاوی اکسيد روی بعد از پرتودهی درصد ژل و در نتيجه استحکام دی‌الکتريک و مقاومت الکتريکی سطحی بالاتری دارند.
| عنوان مقاله به فارسی | بررسي اثر پرتو های الکترونی با انرژی10MeV بر خواص الكتريكي آلياژ EVA/LDPE حاوي ذرات اكسيد روي و دوده |
|---|
Author
Mr
mohammad javad amrollahi
(aeoi)
Peer reviewing
Paper
Paper files: